| Chemical Designation |
Polypropylene either (modified)
|
|||
| DIN Abbreviation |
PPE GF 30
|
|||
| Colour, Filler |
ochre/beige 30% glass fibre
|
|||
| Stock Availabilty | ||||
| Main Characteristics | ||||
| Preferred Fields | ||||
| Applications | ||||
| MECHANICAL | ||||
| Properties |
Unit
|
Test method
DIN ASTM |
||
| Density |
g/cm3
|
53 479
|
1.29
|
|
| Tensile strength/ yield |
MPa
|
53 455
|
||
| Tensile strength/ break |
MPa
|
53 455
|
120
|
|
| Elongation / break |
%
|
53 455
|
02-Mar
|
|
| Modules of elasticity/tension |
MPa
|
53 457
|
9000
|
|
| Modules of elasticity/flexure |
MPa
|
53 457
|
||
| Ball indentation hardness |
MPa
|
53 456
|
||
| Impact strength (charpy) |
kJ/m2
|
53 453
|
08-oct
|
|
| Creep rupture strength /1000 hrs static load |
MPa
|
|||
| Time yield 1% elongation/1000hrs |
MPa
|
47
|
||
| Coefficient of friction/ hardened & ground steel |
-
|
|||
| Wear/ as above |
mm/km
|
|||
| THERMAL | ||||
| Properties |
Unit
|
Test method
DIN ASTM |
||
| Crystaline melting point |
ºC
|
53 736
|
||
| Glass transition temperature |
ºC
|
53 736
|
164
|
|
| Heat distortion temperature | Method A |
ºC
|
ISO 75
|
135
|
| Method B |
ºC
|
ISO 75
|
143
|
|
| Field33 | ||||
| Maximum service temperature | short term |
ºC
|
110
|
|
| long term |
ºC
|
85
|
||
| Coefficient of thermal conductivity |
W/(m.K)
|
|||
| Specific heat |
J(g.K)
|
134
|
||
| Coefficient of thermal expansion |
10-5/K
|
3
|
||
| ELECTRICAL | ||||
| Properties |
Unit
|
Test method
DIN ASTM |
||
| Dielectric constant at 105 HZ |
53 483
|
3.1
|
||
| Dielectric loss factor 105 HZ |
S.cm
|
53 483
|
0.0021
|
|
| Specific volume resistance |
S
|
53 482
|
>1E+15
|
|
| Surface resistance |
53 482
|
|||
| Dielectric strength 1 mm |
KV/mm
|
53 481
|
50
|
|
| Tracking resistance |
53 480
|
KB 250
|
||
| MISCELLANEOUS | ||||
| Properties |
Unit
|
Test method
DIN ASTM |
||
| Moisture absorption |
%
|
53 714 |
0.03
|
|
| Water absorption at saturation at 23 §C |
%
|
53 495 |
0.18
|
|
| Resistance to hot water, washing soda |
limited resistant
|
|||
| Flammibilty | UL 94 |
HB
|
||
| Resistance to weathering |
not resistant,
|
|||
| Compliance | ||||