| Chemical Designation |
Polyphenylene
|
|||
| DIN Abbreviation |
PPS
|
|||
| Colour, Filler |
Black, 10% carbon, graphite, PTFE
|
|||
| Stock Availabilty | ||||
| Main Characteristics | ||||
| Preferred Fields | ||||
| Applications | ||||
| MECHANICAL | ||||
| Properties |
Unit
|
Test method
DIN ASTM |
||
| Density |
g/cm3
|
53 479
|
1.54
|
|
| Tensile strength/ yield |
MPa
|
53 455
|
||
| Tensile strength/ break |
MPa
|
53 455
|
120
|
|
| Elongation / break |
%
|
53 455
|
1.4
|
|
| Modules of elasticity/tension |
MPa
|
53 457
|
12500
|
|
| Modules of elasticity/flexure |
MPa
|
53 457
|
||
| Ball indentation hardness |
MPa
|
53 456
|
||
| Impact strength (charpy) |
kJ/m2
|
53 453
|
20
|
|
| Creep rupture strength /1000 hrs static load |
MPa
|
|||
| Time yield 1% elongation/1000hrs |
MPa
|
0.21
|
||
| Coefficient of friction/ hardened & ground steel |
-
|
0.69
|
||
| Wear/ as above |
mm/km
|
1.2 to 1.9
|
||
| THERMAL | ||||
| Properties |
Unit
|
Test method
DIN ASTM |
||
| Crystaline melting point |
ºC
|
53 736
|
285
|
|
| Glass transition temperature |
ºC
|
53 736
|
88
|
|
| Heat distortion temperature | Method A |
ºC
|
ISO 75
|
|
| Method B |
ºC
|
ISO 75
|
||
| Field33 | ||||
| Maximum service temperature | short term |
ºC
|
260
|
|
| long term |
ºC
|
230
|
||
| Coefficient of thermal conductivity |
W/(m.K)
|
|||
| Specific heat |
J(g.K)
|
|||
| Coefficient of thermal expansion |
10-5/K
|
ab. 3-4
|
||
| ELECTRICAL | ||||
| Properties |
Unit
|
Test method
DIN ASTM |
||
| Dielectric constant at 105 HZ |
53 483
|
|||
| Dielectric loss factor 105 HZ |
S.cm
|
53 483
|
||
| Specific volume resistance |
S
|
53 482
|
||
| Surface resistance |
53 482
|
|||
| Dielectric strength 1 mm |
KV/mm
|
53 481
|
||
| Tracking resistance |
53 480
|
|||
| MISCELLANEOUS | ||||
| Properties |
Unit
|
Test method
DIN ASTM |
||
| Moisture absorption |
%
|
53 714 |
ab. 0.05
|
|
| Water absorption at saturation at 23 §C |
%
|
53 495 | ||
| Resistance to hot water, washing soda |
resistant
|
|||
| Flammibilty | UL 94 |
VO
|
||
| Resistance to weathering |
resistant,
|
|||
| Compliance | ||||