| Chemical Designation |
Acrylinitrile butiadiene styrene
|
|||
| DIN Abbreviation | ||||
| Colour, Filler | ||||
| Stock Availabilty | ||||
| Main Characteristics | ||||
| Preferred Fields | ||||
| Applications | ||||
| MECHANICAL | ||||
| Properties |
Unit
|
Test method
DIN ASTM |
||
| Density |
g/cm3
|
53 479
|
1.06
|
|
| Tensile strength/ yield |
MPa
|
53 455
|
45
|
|
| Tensile strength/ break |
MPa
|
53 455
|
||
| Elongation / break |
%
|
53 455
|
20
|
|
| Modules of elasticity/tension |
MPa
|
53 457
|
2400
|
|
| Modules of elasticity/flexure |
MPa
|
53 457
|
||
| Ball indentation hardness |
MPa
|
53 456
|
90
|
|
| Impact strength (charpy) |
kJ/m2
|
53 453
|
no.br
|
|
| Creep rupture strength /1000 hrs static load |
MPa
|
28
|
||
| Time yield 1% elongation/1000hrs |
MPa
|
17
|
||
| Coefficient of friction/ hardened & ground steel |
-
|
0.5
|
||
| Wear/ as above |
mm/km
|
8.4
|
||
| THERMAL | ||||
| Properties |
Unit
|
Test method
DIN ASTM |
||
| Crystaline melting point |
ºC
|
53 736
|
||
| Glass transition temperature |
ºC
|
53 736
|
85-100
|
|
| Heat distortion temperature | Method A |
ºC
|
ISO 75
|
|
| Method B |
ºC
|
ISO 75
|
96-108
|
|
| Field33 | ||||
| Maximum service temperature | short term |
ºC
|
100
|
|
| long term |
ºC
|
85
|
||
| Coefficient of thermal conductivity |
W/(m.K)
|
0.17
|
||
| Specific heat |
J(g.K)
|
1.2
|
||
| Coefficient of thermal expansion |
10-5/K
|
8
|
||
| MISCELLANEOUS | ||||
| Properties |
Unit
|
Test method
DIN ASTM |
||
| Moisture absorption |
%
|
53 714 |
0.3
|
|
| Water absorption at saturation at 23 §C |
%
|
53 495 |
0.7
|
|
| Resistance to hot water, washing soda |
not resistant
|
|||
| Flammibilty | UL 94 |
HB
|
||
| Resistance to weathering |
not resistant
|
|||
| Compliance | ||||